ABSTRACT
ABSTRACT Objective: The aim of this study is to analyze if both color and nylon fibers have an influence on microwave-cured acrylic resin properties. Methods: Rectangular and disk-shaped specimens were prepared using acrylic resins; medium pink with and without nylon fibers and colorless without nylon fibers. To obtain the rectangular specimens, a stainless steel die was used with the following dimensions: 64 X 10 x 3 mm (± 0.5mm). To obtain disk-shaped specimens, a die 50mm (±0.5mm) in diameter and 0.5mm (±0.05mm) thick was employed. They were randomized to form groups: control (colorless acrylic) and experimental (medium pink, with and without nylon fibers), with each group consisting of ten (10) specimens rectangular in shape and five (5) disk-shaped. They were analyzed in six (6) assays (izod impact strength, n=10; Knoop hardness, n=10; glass transition temperature, n=3; water sorption and solubility, n=5; degree of monomer/polymer conversion, n=1; flexural strength and flexural modulus, n=10). All variables were subjected to the analysis of variance test followed by Tukey's multiple comparison test, at a 5% level of significance. Results: The analysis of the monomer/polymer degree of conversion did not reveal any difference between the three groups of resins (medium pink, with and without nylon fibers and colorless resin); it was approximately 88%. The results did not show significant differences between the groups for each variable (p>0.05). Conclusion: The results showed that color and presence of nylon fibers in acrylic resins did not affect the properties analyzed in this study.
RESUMO Objetivo: Analisar se corantes e fibras de nylon influenciam nas propriedades de uma resina acrílica ativada por energia de micro-ondas. Métodos: Espécimes retangulares e em forma de disco foram confeccionados em resina acrílica rosa médio com e sem fibras de nylon e incolor sem fibras. Para obter os espécimes retangulares, foi utilizada uma matriz de aço inoxidável com as seguintes dimensões: 64 X 10 X 3 (± 0,5mm) e para obter os espécimes em forma de disco, foi utilizada uma matriz com 50mm (± 0,5mm) de diâmetro e 0,5mm (±0,05mm) de espessura. Os mesmos foram randomizados para formar os grupos controle (acrílico incolor sem fibras) e experimentais (rosa médio com e sem fibras), sendo cada grupo composto por dez (10) espécimes retangulares e cinco (5) em forma de disco. Foram os mesmos então submetidos a seis (6) ensaios (resistência ao impacto izod, n=10; dureza knoop, n=10; temperatura de transição vítrea, n=3; sorção e solubilidade, n=5; grau de conversão, n=1; resistência à flexão e módulo de flexão, n=10). Todas as variáveis foram submetidas à análise de variância seguida pelo teste de comparações múltiplas de Tukey, com nível de significância de 5%. Resultados: O grau de conversão foi de 88% para os 3 grupos de resinas e os resultados não mostraram diferença estatisticamente significativa entre os mesmos para cada variável (p>0,05). Conclusão: Os resultados mostraram que o corante e a presença de fibras de nylon em resina acrílica não afetaram as propriedades analisadas nesse estudo.
ABSTRACT
Objective: The objective of this study was to evaluate the effectiveness of disinfection methods in microwave and immersion in peracetic acid in heat-cured, self-cured and microwave-cured acrylic resin, contaminated with Candida albicans.Methods: Five specimens were prepared for each type of acrylic resin. All were infected with Candida Albicans, incubated at 37°C for 24 hours. The group which underwent microwave energy was irradiated with a power of 840W for 1 minute and the other group underwent disinfection by soaking of 0.2% peracetic acid for 5 minutes.Results: All samples proved to be contaminated after the incubation period. After the different processes of disinfection, both immersion in 0.2% peracetic acid as microwave irradiation were effective in disinfection of the 3 types of acrylic resins contaminated by Candida Albicans.Conclusion: Concluded that soaking in 0,2% peracetic acid for 5 minutes with microwave irradiation power 840W for 1 minute are effective methods for disinfecting heat-cured acrylic resin, self-cured acrylic resin and microwave-cured acrylic resin, contaminated with Candida Albicans.
Objetivo: Avaliar a eficácia dos métodos de desinfecção em microondas e imersão em ácido peracético em resina acrílica termopolimerizável, autopolimerizável e resina acrílica polimerizada por microondas, contaminadas com Candida albicans.Métodos: Cinco amostras foram preparadas para cada tipo de resina acrílica. Todas foram infectadas com Candida Albicans, incubadas a 37 ° C durante 24 h. O grupo submetido a energia de microondas foi irradiada com uma potência de 840W durante 1 minuto e o outro grupo foi submetido a desinfecção por imersão de ácido peracético a 0,2% durante 5 minutos.Resultados: Todas as amostras mostraram estar contaminadas depois do período de incubação. Depois dos diferentes processos de desinfecção, tanto a imersão em 0,2% de ácido peracético, como a irradiação de microondas foram eficazes na desinfecção dos 3 tipos de resinas acrílicas contaminados por Candida Albicans.Conclusão: Concluiu-se que a imersão em ácido peracético 0,2% durante 5 minutos e a irradiação de microondas com potência de 840W durante 1 minuto são métodos eficazes para a desinfecção de resina acrílica termopolimerizável, resina acrílica autopolimerizável e resina acrílica polimerizada por microondas, contaminados com Candida Albicans.
ABSTRACT
Introduction Sporothrix schenckii is a thermal dimorphic pathogenic fungus causing a subcutaneous mycosis, sporotrichosis. Nitrocoumarin represents a fluorogenic substrate class where the microbial nitroreductase activity produces several derivatives, already used in several other enzyme assays. The objective of this study was the analysis of 6-nitrocoumarin (6-NC) as a substrate to study the nitroreductase activity in Sporothrix schenckii. Methods Thirty-five samples of S. schenckii were cultivated for seven, 14 and 21 days at 35 °C in a microculture containing 6-nitrocoumarin or 6-aminocoumarin (6-AC) dissolved in dimethyl sulfoxide or dimethyl sulfoxide as a negative control, for posterior examination under an epifluorescence microscope. The organic layer of the seven, 14 and 21-day cultures was analyzed by means of direct illumination with 365 nm UV light and by means of elution on G silica gel plate with hexane:ethyl acetate 1:4 unveiled with UV light. Results All of the strains showed the presence of 6-AC (yellow fluorescence) and 6-hydroxylaminocoumarin (blue fluorescence) in thin layer chromatography, which explains the green fluorescence observed in the fungus structure. Conclusion The nitroreductase activity is widely distributed in the S. schenckii complex and 6-NC is a fluorogenic substrate of easy access and applicability for the nitroreductase activity detection. .
Introdução Sporothrix schenckii é um fungo dimórfico térmico, agente etiológico de micose subcutânea, a esporotricose. Nitrocumarina representa classe de substratos fluorogênicos em que a atividade nitroredutásica microbiana produz vários derivados, já utilizados em vários outros ensaios enzimáticos. O objetivo deste estudo foi analisar 6-nitrocumarina (6-NC) como substrato para estudo da atividade nitroredutásica em Sporothrix schenckii. Métodos Trinta e cinco isolados de S. schenckii foram cultivados por sete, 14 e 21 dias a 35 °C em um microcultivo contendo 6-nitrocumarina ou 6-aminocumarina (6-AC) solubilizada em dimetilsulfóxido ou dimetilsulfóxido como controle negativo, para posterior análise em microscópio de epifluorescência. A fase orgânica da cultura de sete, 14 e 21 dias foi analisada por meio de iluminação direta com luz UV de 365 nm e por eluição em placas de sílica gel G com hexano:acetato de etila 1:4 e revelada com luz UV. Resultados Todos os isolados mostraram a presença de 6-AC (fluorescência amarela) e 6-hidroxilaminocumarina (fluorescência azul) em cromatografia em camada delgada, que explica a fluorescência verde observada na estrutura dos fungos. Conclusão A atividade nitroredutásica é amplamente distribuída no complexo S. schenckii e 6-NC é um substrato fluorogênico de fácil obtenção e aplicabilidade para detecção da atividade nitroredutásica. .
Subject(s)
Coumarins/metabolism , Fluorescent Dyes/metabolism , Nitroreductases/metabolism , Sporothrix/enzymology , Chromatography, Thin Layer , Substrate Specificity , Ultraviolet RaysABSTRACT
A proposta deste estudo foi avaliar a influência de um ciclo de aquecimento em forno de microondas, indicado para desinfecção, sobre a microdureza Knoop e a temperatura de transição vitrea (Tg) de três tipos de resinas acrílicas: termopolimerizável (Classico, Art. Classico, jet, Art, Classico, São Paulo, SP) e polimerizada por energia de microondas (Onda-Cryl, Art, Classico, São Paulo, SP). Para o ensaio de microdureza, foram confeccionados quatro corpos-de-prova de cada tipo de resina acrílica , com 2,2 cm de lado e 2 mm de espessura. Após a obtenção das médias de microdureza, os corpos-de-prova foram submetidos ao ciclo de aquecimento em forno de microondas por um minuto a 850W, sendo então novamente avaliados quanto à microdureza. Para a obtenção da Tg (C), determinada por meio da calorimetria exploratória diferencial (DSC), foram confeccionados seis corpos-de-prova para cada tipo de resina acrílica, nas mesmas dimensões anteriores, sendo três utilizados como controle e três submetidos ao ciclo de aquecimento em forno de microondas durante um minuto a 850W. Os dados foram submetidos ao teste t de Student pareado e os Tg, ao teste t de Student não pareado. Os resultados mostraram um aumento significativo na microdureza para a resina polimerizada por energia de microondas e uma diminuição significativa da Tg para a resina acrílica termopolimerizável. É possivel concluir que um ciclo de aquecimento em forno de microondas aumentou a microdureza da resina de microondas testada e diminuiu a Tg da resina termopolimerizável, servindo de alerta para avaliar com maior cuidado a relação custo/benefício da técnica proposta
Subject(s)
Acrylic Resins , Disinfection , Hardness , Microwaves , Transition TemperatureABSTRACT
The effect of metal complexation on the antimicrobial activity of 1,4-naphthoquinones was investigated. Nickel-, chromium-, iron-, copper-, and cobalt-containing metal chelates of 5-amino-8- hydroxy-1,4-naphtoquinone (2) and its acyl-derivatives (3-8) were synthesized and characterized, and their antimicrobial activity was evaluated. Data from infrared spectroscopy indicate that naphthoquinones coordinate through oxygen and nitrogen atoms for 2, and through oxygen atoms when ligands were acyl derivatives 3-8. Susceptibility tests for antimicrobial activity showed that 2 and its acyl derivatives were effective on inhibiting the growth of pathogenic bacteria such as Staphylococcus aureus, Streptococcus uberis and Bacillus cereus, but not Gram-negative bacteria. The metal complexation often caused decrease of biological activity.Nickel complex of 2 was the most effective against Gram-positive bacteria, showing MIC values ranging from 375 to 1400 mg/ml. Metal chelates may be useful tools for the understanding of the antimicrobial mechanism of 1,4-naphthoquinones on these bacteria